low temperature synthesis of al aln composites from a
low temperature synthesis of al aln composites the ball movement during the milling process is in this work elemental powder of aluminum (99%, 150 mesh) was milled in a dry ammonia atmosphere under a pressure of 3 mpa. the ball to powder ratio was 10/l. the samples were analyzed after 150, 300, and 600 h of milling.